Usage:
- cement-bound grout
- for grouting ceramic tiles and slabs as well as glass mosaic, glass tiles and natural stone
- increased color stability
- for joint widths of 1 – 10 mm
- good flank adhesion
- easy to insert with a long wash window
- no burning
Mixing ratio:
- 1.7 l water: 5 kg powder
- 4.25 l water: 12.5 kg powder
Bulk weight: approx.1.1 kg / l
Fresh weight: approx.1.8 kg / l
Material requirements: with joint width 3 mm, joint depth 5 mm for tiles or. Middle mosaic
| 60 x 60 cm | approx. 0.1 kg / m ² |
| 30 x 60 cm | approx. 0.15 kg / m ² |
| 30 x 30 cm | approx. 0.2 kg / m ² |
| 15 x 15 cm | approx. 0.35 kg / m ² |
| 10 x 10 cm | approx. 0.45 kg / m ² |
| 5 x 5 cm | approx. 0.9 kg / m ² |
The additional losses due to excess material on the tiles are 0.05 – 0.10 kg / m ² depending on the surface quality and working method.
Processing time ( + 20 ° C ): approx. 30 minutes
Accessibility ( + 20 ° C ): after approx. 3 hours
Ball pressure hardness:
- after 1 day approx. 27 N / mm ²
- after 3 days approx. 43 N / mm ²
- after 7/28 days approx. 48 N / mm ²
Suitable for floor heating: Yes
Labeling according to GHS / CLP: see safety data sheet
Labeling according to ADR: see safety data sheet
EMICODE: EC1 PLUS – very low emission PLUS
GISCODE: ZP1 = cement-containing product, low chromate
Packing: Plastic bucket with 5 kg net; Sacks with 12.5 kg net
Storage: in dry rooms approx. Can be stored for 12 months in the original closed container.
Product Code: –
Barcode: –
Container: 12.5 kg paper sack
Color: Brilliance white, Silver Grey, Cement Grey
Mixing ratio: approx. 3.5 l water: 12.5 kg powder corresponding to
approx. 1 part water: 2.75 part powder
Bulk weight: approx. 1.3 kg / l
fresh weight of the mortar: approx. 2.1 kg / l
material requirement : with joint width 3 mm, joint depth 5 mm
for tiles or medium mosaic.
| von 60 x 60 cm ca. 0,10 kg/m² | from 60 x 30 cm approx. 0.15 kg / m 2 |
| von 30 x 30 cm ca. 0,20 kg/m² | von 15 x 15 cm ca. 0,35 kg/m² |
| from 10 x 10 cm approx. 0.50 kg / m 2 | from 5 x 5 cm approx. 1.00 kg / m 2 |
The additional losses due to excess material on the tiles amount to 0.05-0.10 kg / m 2 , depending on their surface properties and method of operation .
Processing time (+20 ° C): approx. 90 minutes
Accessibility (+20 ° C): after approx. 4 hours
ball indentation hardness:
after 1 day approx. 40 N / mm 2
after 3 days approx. 60 N / mm 2
after 7 days approx. 80 N / mm 2
after 28 days approx. 90 N / mm 2 suitability for
underfloor heating: yes
Labeling according to GHS / CLP: see safety data sheet
Labeling according to ADR: see safety
data sheet Packing: bag with 12.5 kg net
Storage: in dry rooms approx. Can be stored for 12 months in the originally sealed container.
Use:
Inside and outside. Floor and wall.
For grouting
- Tiles made of earthenware, stoneware and porcelain stoneware
- Natural and concrete slabs ( insensitive to moisture )
- Fission and clinker plates
- Facade strap
- Blending and visible masonry
- Glass blocks.
For joint widths of 2 – 15 mm.
Colours: gray
Mixing ratio approx.
Component A Component B
2.5 l water 12.5 kg powder
1 RT water 3.4 RT powder
applies to: Joint width 10 mm, joint depth 5 mm for tiles
Material requirements approx.
Length in cm Width in cm Consumption
60 60 0.20 kg / m ²
30 60 0.30 kg / m ²
30 30 0.50 kg / m ²
15 15 1.00 kg / m ²
10 10 1.50 kg / m ²
Note: The additional losses due to excess material on the tiles are 0.05 – 0.10 kg / m ² depending on their surface quality and working method
Bulk weight approx.: 1.50 kg / l
Fresh weight approx.: 2.20 kg / l
Processing time approx.: 90 minute ( n )
Accessibility after approx.: 5 hours ( n )
Application of environmental conditions: + 20 ° C
Ball pressure hardness approx.:
hardness time
60 N / mm ² after 1 day
80 N / mm ² after 3 days
100 N / mm ² after 7 days
120 N / mm ² after 28 days
Floor heating suitability: Yes
Tested according to DIN EN 13888: CG2 A
packaging: Sacks with 12.5 kg net
storage: In dry rooms approx. Can be stored for 12 months in the original closed container.
Use:
Flex joint mortar for wide joints. Indoor and outdoor, on the wall and floor.
ARDEX G 7 FLEX 2-15 is particularly suitable for wide joints and large areas. The high deformability and good flank adhesion reduce stress on thermally stressed surfaces and contribute significantly to the safety of the coverings. After hardening, ARDEX G 7 FLEX has 2-15 water and dirt repellent properties, which ensure a long-lasting beautiful look and thus maintain the value of the coverings. ARDEX G 7 FLEX 2-15 is easy to process, has a high filling power and does not burn up. The area of application includes joints of tiles made of earthenware, stoneware and porcelain stoneware, split and clinker plates as well as non-humid sensitive natural and concrete stone slabs on the wall and floor, indoors and outdoors.ARDEX G 7 FLEX 2-15 meets the requirements CG2 WA according to EN 13888 and is very low in emissions – EC 1 PLUS – according to GEV EMICODE.
PRODUCT HIGHLIGHTS:
- cement-bound flex grout
- ideal for large areas
- highly deformable
- good flank adhesion
- water and dirt repellent
- high strength
- suitable for floor and wall heating
Colours: Gray, Zement grey, Silbergray, Basalt
Mixing ratio approx.
Component A Component B
2.4 l water 12.5 kg powder
1 RT water 4 RT powder
applies to: Joint width 10 mm, joint depth 5 mm for tiles
Material requirements approx.
Length in cm Width in cm Consumption
60 60 0.30 kg / m ²
30 60 0.40 kg / m ²
30 30 0.50 kg / m ²
15 15 1.00 kg / m ²
10 10 1.50 kg / m ²
Note: The additional losses due to excess material on the tiles are 0.05 – 0.10 kg / m ² depending on their surface quality and working method
Bulk weight approx.: 1.40 kg / l
Fresh weight approx.: 2.10 kg / l
Processing time approx.:45 minute ( n )
Accessibility after approx.:90 minute ( n )
Application of environmental conditions: + 20 ° C
Ball pressure hardness approx.:
hardness time
40 N / mm ² after 1 day
50 N / mm ² after 3 days
60 N / mm ² after 7 days
70 N / mm ² after 28 days
Floor heating suitability: Yes
packaging: Sacks with 12.5 kg net
storage: In dry rooms approx. Can be stored for 12 months in the original closed container.
Mixing ratio: approx. 1.1 l water: 5 kg powder corresponding to
approx. 1 part water: 3.4 part powder
Bulk
weight : approx. 1.3 kg / l fresh weight of the mortar: approx. 2.0 kg / l
material requirements: at Joint width 3 mm, joint depth 5 mm
for tiles or medium mosaic .
| for 60 x 60 cm ca. 0,10 kg/m² | for 30 x 60 cm ca. 0,15 kg/m² |
| for 30 x 30 cm ca. 0,20 kg/m² | for 15 x 15 cm ca. 0,35 kg/m² |
| for 10 x 10 cm ca. 0,50 kg/m² | for 5 x 5 cm ca. 1,00 kg/m² |
The additional losses due to excess material on the tiles amount to
0.05–0.10 kg / m² , depending on their surface properties and working method.
Processing time (+20 ° C): approx. 30 minutes
Accessibility (+20 ° C): after approx. 90 minutes
Ball indentation hardness:
after 1 day approx. 40 N / mm²
after 3 days approx. 55 N / mm²
after 7 days approx. 75 N / mm²
after 28 days, approximately 80 N / mm²
floor heating suitability: yes
labeling according to GHS / CLP: see safety
labeling ADR: see safety
packaging: bag with 5 kg of net packed into 4 pieces
storage: Can be stored in dry rooms for approx. 12 months in the originally closed container