Usage:
- cement-bound grout
- for grouting ceramic tiles and slabs as well as glass mosaic, glass tiles and natural stone
- increased color stability
- for joint widths of 1 – 10 mm
- good flank adhesion
- easy to insert with a long wash window
- no burning
Mixing ratio:
- 1.7 l water: 5 kg powder
- 4.25 l water: 12.5 kg powder
Bulk weight: approx.1.1 kg / l
Fresh weight: approx.1.8 kg / l
Material requirements: with joint width 3 mm, joint depth 5 mm for tiles or. Middle mosaic
| 60 x 60 cm | approx. 0.1 kg / m ² |
| 30 x 60 cm | approx. 0.15 kg / m ² |
| 30 x 30 cm | approx. 0.2 kg / m ² |
| 15 x 15 cm | approx. 0.35 kg / m ² |
| 10 x 10 cm | approx. 0.45 kg / m ² |
| 5 x 5 cm | approx. 0.9 kg / m ² |
The additional losses due to excess material on the tiles are 0.05 – 0.10 kg / m ² depending on the surface quality and working method.
Processing time ( + 20 ° C ): approx. 30 minutes
Accessibility ( + 20 ° C ): after approx. 3 hours
Ball pressure hardness:
- after 1 day approx. 27 N / mm ²
- after 3 days approx. 43 N / mm ²
- after 7/28 days approx. 48 N / mm ²
Suitable for floor heating: Yes
Labeling according to GHS / CLP: see safety data sheet
Labeling according to ADR: see safety data sheet
EMICODE: EC1 PLUS – very low emission PLUS
GISCODE: ZP1 = cement-containing product, low chromate
Packing: Plastic bucket with 5 kg net; Sacks with 12.5 kg net
Storage: in dry rooms approx. Can be stored for 12 months in the original closed container.
Product Code: –
Barcode: –
Container: 12.5 kg paper sack
Color: Brilliance white, Silver Grey, Cement Grey
Mixing ratio: approx. 3.5 l water: 12.5 kg powder corresponding to
approx. 1 part water: 2.75 part powder
Bulk weight: approx. 1.3 kg / l
fresh weight of the mortar: approx. 2.1 kg / l
material requirement : with joint width 3 mm, joint depth 5 mm
for tiles or medium mosaic.
| von 60 x 60 cm ca. 0,10 kg/m² | from 60 x 30 cm approx. 0.15 kg / m 2 |
| von 30 x 30 cm ca. 0,20 kg/m² | von 15 x 15 cm ca. 0,35 kg/m² |
| from 10 x 10 cm approx. 0.50 kg / m 2 | from 5 x 5 cm approx. 1.00 kg / m 2 |
The additional losses due to excess material on the tiles amount to 0.05-0.10 kg / m 2 , depending on their surface properties and method of operation .
Processing time (+20 ° C): approx. 90 minutes
Accessibility (+20 ° C): after approx. 4 hours
ball indentation hardness:
after 1 day approx. 40 N / mm 2
after 3 days approx. 60 N / mm 2
after 7 days approx. 80 N / mm 2
after 28 days approx. 90 N / mm 2 suitability for
underfloor heating: yes
Labeling according to GHS / CLP: see safety data sheet
Labeling according to ADR: see safety
data sheet Packing: bag with 12.5 kg net
Storage: in dry rooms approx. Can be stored for 12 months in the originally sealed container.
Use:
Inside and outside. Floor and wall.
For grouting
- Tiles made of earthenware, stoneware and porcelain stoneware
- Natural and concrete slabs ( insensitive to moisture )
- Fission and clinker plates
- Facade strap
- Blending and visible masonry
- Glass blocks.
For joint widths of 2 – 15 mm.
Colours: gray
Mixing ratio approx.
Component A Component B
2.5 l water 12.5 kg powder
1 RT water 3.4 RT powder
applies to: Joint width 10 mm, joint depth 5 mm for tiles
Material requirements approx.
Length in cm Width in cm Consumption
60 60 0.20 kg / m ²
30 60 0.30 kg / m ²
30 30 0.50 kg / m ²
15 15 1.00 kg / m ²
10 10 1.50 kg / m ²
Note: The additional losses due to excess material on the tiles are 0.05 – 0.10 kg / m ² depending on their surface quality and working method
Bulk weight approx.: 1.50 kg / l
Fresh weight approx.: 2.20 kg / l
Processing time approx.: 90 minute ( n )
Accessibility after approx.: 5 hours ( n )
Application of environmental conditions: + 20 ° C
Ball pressure hardness approx.:
hardness time
60 N / mm ² after 1 day
80 N / mm ² after 3 days
100 N / mm ² after 7 days
120 N / mm ² after 28 days
Floor heating suitability: Yes
Tested according to DIN EN 13888: CG2 A
packaging: Sacks with 12.5 kg net
storage: In dry rooms approx. Can be stored for 12 months in the original closed container.
Mixing ratio: approx. 1.1 l water: 5 kg powder corresponding to
approx. 1 part water: 3.4 part powder
Bulk
weight : approx. 1.3 kg / l fresh weight of the mortar: approx. 2.0 kg / l
material requirements: at Joint width 3 mm, joint depth 5 mm
for tiles or medium mosaic .
| for 60 x 60 cm ca. 0,10 kg/m² | for 30 x 60 cm ca. 0,15 kg/m² |
| for 30 x 30 cm ca. 0,20 kg/m² | for 15 x 15 cm ca. 0,35 kg/m² |
| for 10 x 10 cm ca. 0,50 kg/m² | for 5 x 5 cm ca. 1,00 kg/m² |
The additional losses due to excess material on the tiles amount to
0.05–0.10 kg / m² , depending on their surface properties and working method.
Processing time (+20 ° C): approx. 30 minutes
Accessibility (+20 ° C): after approx. 90 minutes
Ball indentation hardness:
after 1 day approx. 40 N / mm²
after 3 days approx. 55 N / mm²
after 7 days approx. 75 N / mm²
after 28 days, approximately 80 N / mm²
floor heating suitability: yes
labeling according to GHS / CLP: see safety
labeling ADR: see safety
packaging: bag with 5 kg of net packed into 4 pieces
storage: Can be stored in dry rooms for approx. 12 months in the originally closed container